Paste for Brazing - Chem Tech Korea

This product can be delivered in the state of power for the welding material of aluminum, copper, and nickel. In other words, it is made to perform the most suitable brazing of components of any shape without being limited by the structure of welding materials.


Type	Size	Key Constituent	Feature	Use
Al-Paste	NFP-100	K, Al, F, Al-powder, BINDER	- For general purpose. Used for in-furnace brazing - Melted at the point of the Al-Si manufacturing process. A wide range of soldering temperature	Used at the time of in-furnace brazing after the application of the part that suggests difficulty in brazing due to the wide gap of its cemented part of aluminum Used at the time of re-brazing after aluminum welding inferiority occurs
Al-Paste	NFP-200	K, Al, F, Al-powder, BINDER＋catalyst	- Melted at the point of the Al-Si manufacturing process. Excellent flowability of its filler.
Flux Paste of the Fluoridation	NFP-300	K, Al, F, BINDER＋catalyst	- Mixed with the flowability additive of the fluoridation line. No need of removing and cleaning after brazing	Used at the time of application of high density Al-flux Welding material for torch welding of aluminum pipe components.
Flux Paste of the Chloride	CFP-100	Li, Na, Zn, Cl, BINDER	- Flux of a low paste. Good flowability and permeability.	Manual torch or automatic torch welding. Welding material for machine Al-Flux
Cu-Paste	TPC-3600	Cu(Y), Additive, BINDER	- High intensity and fine flowability - 1000-1200℃ of melting temperature	Welding material for the high temperature brazing of steel or steel casting
Cu-Paste	TPC-3310	Cu(B), Additive, BINDER	- Suitable for brazing of all conditions in atmosphere	Welding material for copper and copper alloys
Ni-Paste	TNP-100	Ni,Additive ,BINDER	- Ni alloy. Powder state. Excellent welding performance with good flowability	Welding material of the high temperature brazing of special metals